Specimen preparation for tem

ABSTRACT

A specimen kit having a tiny chamber is disclosed for a specimen preparation for TEM. The space height of the chamber is far smaller than dimensions of blood cells and therefore is adapted to sort nanoparticles from the blood cells. The specimen prepared under this invention is suitable for TEM observation over a true distribution status of nanoparticles in blood. The extremely tiny space height in Z direction eliminates the possibility of aggregation of the nanoparticles and/or agglomeration in Z direction during drying; therefore, a specimen prepared under this invention is suitable for TEM observation over the dispersion and/or agglomeration of nanoparticles in a blood.

BACKGROUND

1. Technical Field

The present invention relates to a specimen preparation suitable for observation under a Transmission Electron Microscopy (TEM), which reflects a true distribution status, dispersion and/or agglomeration, of the nanoparticles in a sample blood.

2. Description of Related Art

FIG. 1A˜1E is a first specimen prepared according to a traditional method

FIG. 1A shows a traditional substrate 10, usually a piece of copper grids, is prepared.

FIG. 1B shows a drop of sample blood 11 is placed on a top surface of the substrate 10. The sample blood 11 contains, among others, nanoparticles 11N, and blood cells 11C. The average diameter of a red blood cell (RBC) is 6 to 8 micrometers. The average diameter of a white blood cell (WBC) is 10 to 12 micrometers. A blood cell 11C has a dimension in um which is greatly larger than a dimension of a nanoparticle.

FIG. 1C shows the sample blood 11 evaporates during drying, the blood drop shrinkages and a plurality of smaller droplet is then formed. The surface tension 13 of each droplet drags the components therein closer and closer. A gathering of the components is undergoing.

FIG. 1D shows two groups of aggregation A1 of nanoparticles 11N, as an example, are formed. Please pay attention to the concentration effect of the components within each droplet caused by surface tension 13 during drying, which causes the aggregation A1 of nanoparticles. The aggregation A1 of nanoparticles on the prepared sample displays a similar appearance to a nanoparticle-agglomeration; this causes observation confusion between the two, aggregation and agglomeration, and gives wrong information under TEM observation to the observer.

FIG. 1E shows a top view of FIG. 1D. Two groups of aggregation A1 of nanoparticles 11N are formed, as an example. The specimen of FIG. 1E does not reflect the true status for the nanoparticles 11N, the nanoparticles 11N is even dispersed in the sample blood 11 as evidenced by FIG. 1B.

Now, let's pay attention to the nanoparticles 11N only, one of the purposes to examine the specimen of a sample blood is to observe the status, dispersion and/or agglomeration, of the nanoparticles 11N in the original sample blood. However, the traditional specimen preparation does not reflect the original or true status, dispersion and/or agglomeration, of the nanoparticles 11N in the original sample blood, as shown in FIGS. 1D-1E where aggregation A1 of nanoparticles 11N, false information has been displayed under the TEM observation due to surface tension 13 of the droplets during drying. It is hoped that a true status, dispersion and/or agglomeration, of the nanoparticles 11N can be reflected in the original sample blood.

FIG. 2A-2E is a second specimen prepared according to a traditional method

FIG. 2A shows a traditional substrate 10, copper grids, is prepared.

FIG. 2B shows a drop of sample blood 11 is placed on a top surface of the substrate 10. The sample blood 11 contains, among others, dispersed nanoparticles 11N, nanoparticle-agglomeration 11NA, and blood cells 11C.

FIG. 2C shows the liquid evaporates during drying, the blood drop shrinkages, and smaller droplets are then formed. The surface tension 13 of each droplet drags the components therein closer and closer.

FIG. 2D shows aggregation A2 of nanoparticles are formed.

FIG. 2E shows a top view of FIG. 2D. Two groups of aggregation A2 of nanoparticles 11N are formed. In actual, the aggregation A2 does not exist in the original sample blood, see FIG. 2B, and the specimen of FIG. 2E gives false information to the observer.

Now, let's pay attention to the nanoparticle-agglomeration 11NA only, one of the purposes to examine the specimen of a sample blood under TEM is to observe whether any nanoparticle-agglomeration exists in the original sample blood. However, the traditional specimen preparation does not reflect the true numbers of nanoparticle-agglomeration 11NA; several aggregation A2 of nanoparticles 11N, a counterfeit to nanoparticle-agglomeration 11NA, are presented in FIGS. 2D˜2E. The aggregation A2 is caused by the surface tension 13 of droplets during drying. It is hoped that a true situation for the nanoparticles, dispersion and/or agglomeration, can be observed over the specimen.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1A˜1E is a first specimen prepared according to a traditional method

FIGS. 2A˜2E is a second specimen prepared according to a traditional method

FIGS. 3A˜3E is a first specimen prepared according to the present invention

FIGS. 4A˜4E is a second specimen prepared according to the present invention

FIG. 5 is a perspective view of a specimen kit.

FIG. 6 is a section view of a first specimen kit according to the present invention

FIGS. 7A˜7B is a chamber for a first specimen kit

FIGS. 8A˜8B is a chamber for a second specimen kit

FIGS. 9A˜9B is a chamber for a second specimen kit

DETAILED DESCRIPTION OF THE INVENTION

This invention discloses a specimen preparation through a specimen kit which has a tiny chamber. The space height of the chamber is configured far smaller than a diameter of a RBC, since a RBC is smaller than a WBC, so that all the blood cells can be screened from entering the chamber of the specimen kit. The absence of the blood cells in the specimen reduces interference for the observation over the nanoparticles, and therefore enhances the quality and quantity check over the specimen. The small chamber of the specimen kit limits the sample blood inside, eliminates surface tension effect during drying. The specimen preparation as disclosed in this invention makes it possible to detect a truly distribution status of the nanoparticles, dispersion and/or agglomeration, in the original sample blood.

FIGS. 3A-3E is a first specimen prepared according to the present invention

FIG. 3A shows a sample blood 11 is ready to inject into a chamber 20 of a specimen kit. The sample blood 11 contains nanoparticles 11N and blood cells 11C. The chamber 20 is formed in between a top substrate 20T and a bottom substrate 20B. The space height h between the top substrate 20T and the bottom substrate 20B is made less than a diameter of an RBC so that all the RBC and WBC can be screened from entering the chamber 20. A space height of 10 um for the chamber 20 is enough for a TEM observation over the distribution status of the nanoparticles, dispersion and/or agglomeration, in a sample blood.

FIG. 3B shows nanoparticles 11N enter the chamber 20 with the sample blood 11. The blood cell 11C does not enter the chamber 20 due to its larger dimension.

FIG. 3C shows a drying process is performed to the sample blood 11 of FIG. 3B. The sample blood 11 within the chamber 20 is dried, a plurality of small droplets formed. Each droplet wraps a single nanoparticle 11N and attaches onto the inner surfaces of the chamber 20 due to an adhesion force 13 of the droplet.

FIG. 3D shows some nanoparticles 11N attaches to a bottom surface of the top substrate 20T after drying, and some nanoparticles 11N attaches to a top surface of the bottom substrate 20B after drying. However, due to the tiny space height h between the two substrates 20T, 20B. The tiny space height h limits the number of the nanoparticles 11N distributed in Z direction and hence, eliminates the possibility of aggregation of the nanoparticles 11N in Z direction.

FIG. 3E shows a top view of FIG. 3D. Dispersed nanoparticles 11N shown in FIG. 3E displays a real dispersion status of the nanoparticles 11N in the original sample blood 11 as can be seen in FIG. 3B.

FIGS. 4A˜4E is a second specimen prepared according to the present invention

FIG. 4A shows a sample blood 11 is ready to inject into the chamber 20 of a specimen kit. The sample blood 11 contains nanoparticle-agglomeration 11NA, nanoparticles 11N, and blood cells 11C. The chamber 20 is formed in between a top substrate 20T and a bottom substrate 20B. The space height h between the top substrate 20T and the bottom substrate 20B is made less than a diameter of an RBC so that all the blood cells 11C can be screened from entering the chamber 20.

FIG. 4B shows both the nanoparticles 11N and the nanoparticle-agglomeration 11NA enter the chamber 20 with the sample blood 11. The blood cell 11C does not enter the chamber 20 due to its larger dimension.

FIG. 4C shows a drying process is performed to the sample blood 11 of FIG. 4B. The sample blood 11 within the chamber 20 is dried, a plurality of small droplets formed. Each droplet wraps a single nanoparticle and attaches onto the inner surfaces of the chamber 20 due to an adhesion force 13 of the droplet.

FIG. 4D shows some nanoparticles 11N and nanoparticle-agglomeration 11NA attach to a bottom surface of the top substrate 20T, and some nanoparticles 11N and nanoparticle-agglomeration 11NA attach to a top surface of the bottom substrate 20B after drying. The tiny space height h limits the number of the nanoparticles 11N and nanoparticle-agglomeration 11NA distributed especially in Z direction, and hence eliminates the possibility of aggregation of the nanoparticles 11N and the nanoparticle-agglomeration 11NA in Z direction.

FIG. 4E shows a top view of FIG. 4D. The dispersed nanoparticles 11N and nanoparticle-agglomeration 11NA on the specimen displays a real situation of the nanoparticles 11N and nanoparticle-agglomeration 11NA distributed in the original sample blood 11 as can be seen in FIG. 4B.

FIG. 5 is a perspective view of a specimen kit.

FIG. 5 shows a specimen kit suitable for a specimen preparation for observation under a TEM. The kit has a chamber 20 formed in between a top substrate 20T and a bottom substrate 20B; a space height h of the chamber 20 is made smaller than a diameter of an RBC; and the top substrate 20T is made of a material transparent to electron. A space height of 10 um is enough for a TEM observation over the distribution status of the nanoparticles, dispersion and/or agglomeration, in a sample blood 11. A spacer 22 is inserted in between the substrates to control the space height. Sample solution entrance 26 is configured for sampling injection. Observation window 25 is made in the top center of a frame 24 of the kit. Partial of the chamber 20 exposes within the window 25 for TEM observation from top of the kit.

FIG. 6 is a section view of a first specimen kit according to the present invention

FIG. 6 shows the chamber 20 is formed in between a top substrate 20T and a bottom substrate 20B. Observation window 25 is made on the top center of a frame 24 of the kit. Partial of the chamber 20 exposes within the window 25 for TEM observation from top of the kit. Sample solution entrance 26 is configured for sample injection.

FIGS. 7A˜7B is a chamber for a first specimen kit

FIG. 7A shows a top view of the chamber 20 for the first specimen kit. A top substrate 20T made of a flat panel transparent to electron is viewed. FIG. 7B shows a section view of FIG. 7A, where both the top substrate 20T and the bottom substrate 20B are viewed, and a sample blood 11 is filled in the chamber between the substrates 20T, 20B.

FIGS. 8A˜8B is a chamber for a second specimen kit

FIG. 8A shows a top view of the chamber for the second specimen kit. A top substrate 30T is viewed. A plurality of through hole 31 is made in the top substrate 20T. For some other purposes, observation is made over the specimen with blood or liquid in the chamber, under such circumstances, a better observation quality can be displayed through the hole 31 without the hindrance of the top substrate 20T when observation is made through TEM over the specimen.

FIG. 8B shows a section view of FIG. 8A where both the top substrate 20T and the bottom substrate 20B are viewed, a sample blood 11 is filled in the chamber between the substrates 20T, 20B. FIG. 8B shows each hole is configured small enough to be able to hold the sample blood 11 staying in the chamber by surface tension 33, so that the sample blood 11 does not seep through the hole 31.

FIGS. 9A˜9B is a chamber for a second specimen kit

FIG. 9A shows a top view of the chamber for the third specimen kit. A top substrate 40T is viewed. A plurality of through groove 41 is made in the top substrate 40T. For some other purposes, observation is made over the specimen with blood or liquid in the chamber, under such circumstances, a better observation quality can be displayed through the groove 41 without the hindrance of the top substrate 20T when observation is made through TEM over the specimen.

FIG. 9B shows a section view of FIG. 9A where both the top substrate 40T and the bottom substrate 40B are viewed, a sample blood 11 is filled in the chamber between the substrates 40T, 40B. FIG. 9B shows each through groove 41 is configured small enough to be able to hold the sample blood 11 staying in the chamber by surface tension 43, so that the sample blood 11 does not seep through the groove 41.

While several embodiments have been described by way of example, it will be apparent to those skilled in the art that various modifications may be configured without departing from the spirit of the present invention. Such modifications are all within the scope of the present invention, as defined by the appended claims. 

What is claimed is:
 1. A specimen preparation for TEM, comprising: preparing a sample blood, containing nanoparticles; preparing a specimen kit, having a top substrate and a bottom substrate; filling the sample blood into a chamber between the substrates; and drying the blood, leaving the nanoparticles precipitated; wherein a space height of the chamber, being smaller than a diameter of a blood cell; and the top substrate, being made of a material transparent to electron.
 2. A specimen preparation for TEM as claimed in claim 1, wherein the blood cell is selected from a group consisted of white blood cell and red blood cell.
 3. A specimen preparation for TEM as claimed in claim 1, wherein the space height is less than 10 um.
 4. A specimen preparation for TEM as claimed in claim 1, further comprising: a hole, being made in the top substrate, and being small enough to be able to hold the sample blood staying in the chamber by surface tension before drying.
 5. A specimen preparation for TEM as claimed in claim 1, further comprising: a through groove, being made in the top substrate, and being small enough to be able to hold the sample blood staying in the chamber by surface tension before drying.
 6. A specimen kit for TEM, comprising: a top substrate and a bottom substrate; a chamber, formed between the substrates; wherein a space height of the chamber, being smaller than a diameter of a blood cell; and the top substrate, being made of a material transparent to electron.
 7. A specimen kit for TEM as claimed in claim 6, wherein the blood cell is selected from a group consisted of white blood cell and red blood cell.
 8. A specimen kit for TEM as claimed in claim 6, wherein the space height is smaller than 10 um.
 9. A specimen kit for TEM as claimed in claim 6, further comprising: a through hole, made in the top substrate, being small enough to be able to hold the sample blood staying in the chamber by surface tension before drying.
 10. A specimen preparation for TEM as claimed in claim 6, further comprising: a through groove, made in the top substrate, being small enough to be able to hold the sample blood staying in the chamber by surface tension before drying. 